Thermal Decomposition of Degassed Barium Titanyl Oxalate: In Comparison to the Solid-State Reaction Mechanism

Buy Article:

$51.00 plus tax (Refund Policy)

Abstract:

This study examined the formation of BaTiO3 from degassed barium titanyl oxalate (degassed BTO), which was heat treated at 500°C for 2 h followed by 20 min of aqueous milling, upon further heating. The evolution of BaCO3, Ti-based interphase and BaTiO3 at various temperatures was examined by X-ray diffraction, high-resolution scanning transmission electron microscopy, and electron energy loss spectroscopy. When the degassed BTO was exposed to an aqueous milling, significant amounts of needle-shaped BaCO3 crystals formed preferentially, which made this system similar to that of a solid-state reaction. However, the formation mechanism of BaTiO3 observed in this study was found to be different from that of a solid-state reaction due to the different nature of the Ti-based phase.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/j.1551-2916.2010.04064.x

Affiliations: 1: School of Materials Science and Engineering, Yeungnam University, Gyeongsan 712-749, Korea 2: Instrumental Analysis Center, Yeungnam University, Gyeongsan 712-749, Korea 3: Nano Materials Team, Samsung Fine Chemicals Co. Ltd., Daejeon 305-380, Korea

Publication date: January 1, 2011

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Partial Open Access Content
Partial Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more