Piezoelectric Properties of PZT-Based Ceramic with Highly Aligned Pores

Buy Article:

$51.00 plus tax (Refund Policy)

Abstract:

Porous lead zirconate titanate–lead zinc niobate (PZT–PZN) piezoelectric ceramics with a high degree of pore alignment were fabricated using directional freeze casting of a ceramic/camphene slurry. Well-aligned pores were formed as the replica of the camphene dendrites that grew in a preferential orientation, while a high porosity of 90% was achieved by employing a low initial solid loading of 5 vol%. As the orientation angle of the pores to the poling direction was decreased, the hydrostatic piezoelectric properties, such as hydrostatic piezoelectric strain coefficient (dh), the hydrostatic piezoelectric voltage coefficient (gh), and the hydrostatic figure of merit, increased significantly. The sample containing pores aligned parallel to the poling direction showed an extremely high HFOM of 161019 × 10−15 Pa−1, which was ∼1300 times higher than that (124 × 10−15 Pa−1) of the dense sample, owing to the presence of aligned pores.

Document Type: Research Article

DOI: https://doi.org/10.1111/j.1551-2916.2008.02359.x

Affiliations: 1: School of Material Science and Engineering, Seoul National University, Seoul 151-742, Korea 2: Department of Dental Laboratory Science and Engineering, Korea University, Seoul 136-703, Korea

Publication date: 2008-06-01

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more