Self‐Healing of an Epoxy Resin Using Scandium(III) Triflate as a Catalytic Curing Agent

Buy Article:

$43.00 plus tax (Refund Policy)


A novel Lewis acid‐catalysed self‐healing system is investigated for implementation into epoxy‐based fibre reinforced polymer (FRP) composite materials. The catalyst, scandium(III) triflate, is selected using a qualitative approach and subsequently embedded with pre‐synthesised epoxy‐solvent loaded microcapsules, into an epoxy resin. Healing is initiated when microcapsules are ruptured at the onset of crack propagation. The epoxy monomer healing agent contained within actively undergoes ring‐opening polymerisation (ROP) on contact with the locally dispersed catalyst, forming a new polymer to bridge the two fractured crack planes. Self‐healing performance is quantified using a tapered double cantilever beam (TDCB) test specimen and the effects of microcapsule content and healing temperature and time are all independently considered. As an initial ‘proof of concept’ study, results show that a material recovery value of greater than 80% fracture strength is achieved for this novel Lewis acid‐catalysed self‐healing epoxy resin.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Affiliations: 1: Advanced Composite Centre for Innovation and Science (ACCIS), Department of Aerospace Engineering, University of Bristol, Queen's Building, University Walk, Bristol, BS8 1TR, UK 2: School of Chemistry, University of Bristol, Cantock's Close, Bristol, BS8 1TS, UK

Publication date: 2011-12-20

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more