Effect of Bimodal Size Distribution on Optical Properties of CdSe Nanocrystals

$71.00 plus tax (Refund Policy)

Buy Article:

Abstract:

Effect of bimodal size distribution (BSD) on optical properties of electrodeposited CdSe nanocrystalline thin films is reported. Grazing angle X-ray diffraction identifies two different nanocrystalline size regimes with both compressive and tensile strains coexisting in the same sample. The two size regimes change their size with the change of electrodeposition current density or temperature. Optical absorption studies reveal two absorption edges corresponding to the two different sizes. Presence of two well separated photoluminescence (PL) bands due to excitonic recombination supports the presence of BSD in the sample which is also confirmed from temperature dependent PL measurements. The origin of the two PL bands are attributed to the transfer of thermally activated carriers between two size regimes accompanied by excitonic recombination. Micro Raman scattering of nanocrystalline CdSe at 300K showed softening of Raman phonon modes due to small size nanocrystallites but do not reflect the BSD effect.





More about this publication?
  • Current Nanoscience publishes authoritative reviews and original research reports, written by experts in the field on all the most recent advances in nanoscience and nanotechnology. All aspects of the field are represented including nano- structures, synthesis, properties, assembly and devices. Applications of nanoscience in biotechnology, medicine, pharmaceuticals, physics, material science and electronics are also covered. The journal is essential to all involved in nanoscience and its applied areas.
Related content

Tools

Favourites

Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more