Sr0.95Zn0.05Se:Eu2+ and CdSe/ZnS Nanocrystals Hybrid Phosphors for Enhancing Color Rendering Index of White Light Emitting Diode
Abstract:In this study, the yellow emitting cubic structure of Sr0.95Zn0.05Se:Eu2+ phosphors were prepared by high temperature solid state reaction. The Sr0.95Zn0.05Se:Eu2+ phosphors exhibited strong excitation intensity under 400–460 nm region, and broad band emission appeared at around 545–600 nm due to the d–f transition of Eu2+. To enhance the red emission, HDA/TOP/TOPO capped CdSe/ZnS NCs were synthesized via fast nucleation and slow growth method. The narrow emission peak was located at 615 nm with 69% of high quantum yield. Bright white emission was generated by combining a 460 nm InGaN LED chip with CdSe/ZnS NCs and Sr0.95Zn0.05Se:Eu2+ hybrid phosphors. The fabricated white LEDs showed warm white light with acceptable CIE chromaticity coordinate variation from (0.343, 0.255) at 20 mA to (0.335, 0.250) at 50 mA. The addition of CdSe/ZnS NCs contributed to the extension of white light spectrum by supplement of the red region. The color rendering index was largely enhanced from 41.7 to 79.7 compared to the Sr0.95Zn0.05Se:Eu2+ based phosphors white LED.
Document Type: Research Article
Publication date: 2012-07-01
More about this publication?
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites