Study on Luminescence Behavior of BaAl12O19:Tb, Eu
Abstract:BaAl12O19:Tb, Eu phosphors were prepared by sol–gel technique. The luminescence properties and the energy transfer between Eu2+ and Tb3+ were investigated. For BaAl12O19:Tb phosphor, the strongest excitation peak and emission peak produced from Tb3+ transition of 5D4–7F5 were at 240 nm and at 550 nm respectively, while the peak shape was narrow and peak intensity was large. The Eu2+ added in the BaAl12O19:Tb induced energy transfer to Tb3+ and different color luminescence from blue (400 nm) to green (570 nm) was obtained by changing the ratio of Tb3+/Eu2+ with excitation at 240 nm.
Document Type: Research Article
Publication date: November 1, 2011
More about this publication?
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- ingentaconnect is not responsible for the content or availability of external websites