Gasochromic Switching of Ta and Pd-Doped Nanocrystalline TiO2 Thin Films

$113.00 plus tax (Refund Policy)

Buy Article:


In this work TiO2:(Ta, Pd) thin films with gasochromic properties have been described. Thin films were prepared by reactive magnetron sputtering process using mosaic Ti–Ta–Pd target. The amounts of dopants were 2.54 at.% and 12.36 at.% of Ta and Pd, respectively. The results of optical measurements performed at presence of ethanol and additional heating of the sample up to 350 °C have shown an abrupt change of transmission level from 80% down to 10% in VIS and in IR range. The gasochromic change was very fast. Moreover, rapid cooling (down to room temperature) in an air ambient results in stable thin film coloration. The reverse effect (bleaching) was obtained after annealing at 500 °C in an ambient air.


Document Type: Research Article

DOI: http://dx.doi.org/10.1166/jnn.2011.3472

Publication date: October 1, 2011

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • ingentaconnect is not responsible for the content or availability of external websites
Related content



Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more