Structure of BaO on Hierarchical Macro-Meso-Microporous Alumina and Its Effect of Interaction with Pt Nanoparticle on NO2 Desorption

Buy Article:

$113.00 plus tax (Refund Policy)


Recently, the lean NO x trap technology using supported Pt catalyst on alumina was devised to store NO x under lean condition and to reduce into N2 and water under rich condition in lean burn engine. In this work, the effect of the Pt nanoparticle supported on hierarchical macro-meso-microporous BaO-Al2O3 on NO2 desorption has been investigated with NO2 temperature programmed desorption, TEM, SEM, TGA and hydrogen chemisorption. Crystalline BaO phase of 20–30 nm thickness were obtained on the hierarchical macro-meso-microporous Al2O3 with a simple impregnation of Ba(NO3)2 and Ba(ClO4)2. The interaction of Pt and BaO was resulted in the formation of atomically dispersed Pt nanoparticles and also decreased the desorption temperature of NO2 adsorbed on BaO at much lower temperature than that from the BaO-Al2O3 support only. This synergistic lowering of NO2 desorption temperature may be originated from the interaction between Pt and BaO.


Document Type: Research Article


Publication date: 2011-08-01

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more