Temperature Dependent Emission Quenching for Silicon Nanoclusters

Buy Article:

$113.00 plus tax (Refund Policy)


Silicon reach-silicon-oxide (SRSO) film containing silicon nanoclusters was obtained by the reactive magnetron sputtering. Photoluminescence (PL) spectra were measured as a function of temperature at different excitation wavelengths and additionally at different excitation power densities. Obtained PL spectra characterize by two emission bands centered at 1.6 and 2.4 eV. For these bands, temperature behaviour of PL intensities strongly differs but clearly correlate each other. Moreover, it has been observed that obtained PL intensities versus temperature exhibit a strong dependence on the excitation power density in the low temperature range.


Document Type: Research Article


Publication date: 2010-09-01

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more