Preparation of Born-Doped a-SiC:H Thin Films by ICP-CVD Method and to the Application of Large-Area Heterojunction Solar Cells

$113.00 plus tax (Refund Policy)

Buy Article:


Hydrogenated amorphous silicon carbide (a-SiC:H) film has been widely used as an emitter p layer in solar cells. For the better p layer, wide optical bandgap, and high electrical conductivity should be obtained from the effective method. We prepared the boron-doped a-SiC:H thin films using inductively coupled plasma chemical vapor deposition (ICP-CVD) method and characteristics on the small-area (2 cm × 2 cm) as well as the large-area films (diameter of 100 mm) were shown on it. As a substrate, the n-type (100) oriented CZ c-Si (5.5∼6.5 Ω·cm, 650 m) wafers were used and cleaned by using the reduced RCA method. A silane (SiH4) of 99.999% purity, H2 and 60% hydrogen diluted ethylene (C2H4) was used as source gas for the deposition of intrinsic a-SiC:H films, and then diborane (B2H6), as the doping gas, is added to C2H4 and SiH4/H2 during the deposition of films. The uniformity of thickness and optical bandgap from large-area as-dep. films was at 1.8% and 0.3%, respectively. Heterojunction solar cell with 2 wt%-AZO/p-a-SiC:H/i-a-Si:H/c-Si/Ag structure was fabricated and characterized with diameter of 152.3 mm in this large-area ICP-CVD system. Conversion efficiency of 9.123% was achieved with a practical area of 100 mm × 100 mm, which can show the potentials to the fabrication of the large-area solar cell using ICP-CVD method.
More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • ingentaconnect is not responsible for the content or availability of external websites
Related content



Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more