The Synthesis of BaMgAl10O17:Eu2+ Nanorods and Their Luminescence Properties Under UV and VUV Excitation

Buy Article:

$105.00 plus tax (Refund Policy)

BaMgAl10O17:Eu2+ nanorods were synthesized by the sol–gel process at 1,250 °C, while bulk phosphor was prepared by conventional solid-state reaction at 1,600 °C. The naonrods had a homogeneous grain size 80–100 nm in diameter and 0.8–1 μm in length. Under 254 nm excitation, the emission intensity of these nanorods was 90.12% of the commercial phosphor. Under 147 nm excitation, the intensity rate was 78.15%. The color coordinates were (0.145, 0.062) under ultraviolet (UV) excitation and (0.143, 0.068) under VUV excitation. Compared with the standard blue fluorescence (0.14, 0.08), the y value was obviously decreasing. These low y values suggested that these BAM nanorods were good for restricting the decrease of BAM effciency during heating.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
No Metrics


Document Type: Research Article

Publication date: 2010-03-01

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more