Magnetically Responsive Phase-Change Microspheres with Large Magnetization Using Ferrite Nanoparticles
Abstract:Magnetically responsive phase-change microspheres were prepared and studied in this article. In the synthetic process, oleic acid was used to modify the iron oxide nanoparticles. The ferrite nanoparticles, about 10 nm in diameter, were highly dispersed due to the oleic acid on the surface of the particles, and they were encapsulated in polymethyl methacrylate (PMMA) by microemulsion polymerization with paraffin, which could be presumed from the differential scanning calorimetry (DSC) curves. According to the morphology in the scanning electron microscopy (SEM) image, the average diameter of the microspheres was about 200 nm, a large amount of nano-sized ferrite can be observed in a transmission electron microscope (TEM) image showing the structure of the microspheres. Finally, in the magnetization curve from a vibrating sample magnetometer, the saturation magnetization of microspheres was 12.2 emu/g, which was effective in the compatibility of infrared simulation and microwave absorption.
Document Type: Research Article
Publication date: March 1, 2010
More about this publication?
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites