Nanocasted Synthesis of the Mesostructured LaCoO3 Perovskite and Its Catalytic Activity in Methane Combustion

$113.00 plus tax (Refund Policy)

Buy Article:


Extremely high surface area, mesostructured LaCoO3 perovskite has been synthesized by nanocasting from mesoporous cubic (Ia3d) vinyl silica. Thus-prepared material was characterized by XRD, TEM, and N2-sorption, and its catalytic property was also tested in methane combustion. The catalytic results demonstrated that thus-prepared mesostructured LaCoO3 perovskite had higher activity than the conventional bulk LaCoO3 perovskite prepared by citrate method. Further analysis showed that both the high surface area and the existence of high valent cobalt ions (Co4+, XPS analysis) were contributed to the high activity.


Document Type: Research Article


Publication date: February 1, 2009

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • ingentaconnect is not responsible for the content or availability of external websites
Related content



Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more