Synthesis and Photoluminescent Properties of Nanocrystalline CaMoO4 Thin Film via Chemical Solution Processing

Buy Article:

$113.00 plus tax (Refund Policy)

Abstract:

Stoichiometric CaMoO4 thin film was successfully fabricated based on chemical solution processing. The thin films were deposited on Si(100) substrates by means of the spin-coating technique. X-ray diffraction reveals that the CaMoO4 thin film prepared are pure and well crystalline thin films. Atom Force Microscope photographs indicate that the film prepared possesses a homogeneous and dense surface morphology. The average grain size of the films was 40–50 nm, and the root-mean-square (RMS) of the surface roughness and the average surface roughness of the film measured were 2.161 nm and 1.726 nm respectively. The photoluminescent properties of calcium molybdate thin film under ultraviolet light excitation were systematically measured from 12 K to room temperature and a green emission band of the films were observed. The results of present work confirm that the chemical solution processing is a promising technology on the fabrication of CaMoO4 thin film.

Keywords: CALCIUM MOLYBDATE; LUMINESCENT PROPERTIES; SOFT SOLUTION PROCESSING; THIN FILM

Document Type: Research Article

DOI: https://doi.org/10.1166/jnn.2008.422

Publication date: 2008-05-01

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free ContentFree content
  • Partial Free ContentPartial Free content
  • New ContentNew content
  • Open Access ContentOpen access content
  • Partial Open Access ContentPartial Open access content
  • Subscribed ContentSubscribed content
  • Partial Subscribed ContentPartial Subscribed content
  • Free Trial ContentFree trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more